Titel: Electrical and structural characterization of (KxNa1-x)NbO3 ceramics modified with Li and Ta
Sprache: English
Autor/Autorin: Mgbemere, Henry Ekene 
Hinterstein, Jan Manuel 
Schneider, Gerold A. 
Schlagwörter: (KxNa1-x)NbO3;Ferroelektrische Keramik;die Synchrotronstrahlung;(KxNa1-x)NbO3;ferroelectric ceramics;phase transition;synchrotron radiation
Erscheinungsdatum: 2011
Quellenangabe: Journal of applied crystallography ; 44.2011, pp, 1080-1089
Zusammenfassung (englisch): (KxNa1-x)NbO3 ceramics modified with Li+ and Ta5+ have been produced using the mixed-oxide synthesis method. Synchrotron X-ray diffraction measurements were made on the samples from 12K to temperatures above their ferroelectric-paraelectric transition points with 10K measurement steps. Rietveld refinement using FULLPROF suite was used to refine the patterns. Depending on the composition and temperature, rhomhohedral phases, orthorhombic phases, tetragonal phases, cubic phases and two-phase mixtures were obtained. R3c (161), Amm2 (38), P4mm (99), (221) space groups and their combinations were used to refine the rhombohedral, orthorhombic, tetragonal, cubic and the mixed phases respectively. Li+ addition suppressed the formation of the rhombohedral low temperature phase and increased the Curie temperature. This is attributed to size difference in ionic radii of the A-site elements which leads to increased atomic polarizability and increased interaction with the B-site element. Li+ and Ta5+ co-doping led to a wide temperature range of phase coexistence between the orthorhombic and tetragonal phase. Electrical characterizations by dielectric and hysteresis measurements were used to compare with the results from the structural studies.
URI: http://tubdok.tub.tuhh.de/handle/11420/1036
DOI: 10.15480/882.1034
Institut: Keramische Hochleistungswerkstoffe M-9 
Dokumenttyp: ResearchPaper
Enthalten in den Sammlungen:tub.dok

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat
Manuscript_KNN_Li_Ta.pdf1,25 MBAdobe PDFMiniaturbild
Öffnen/Anzeigen
Zur Langanzeige

Seitenansichten

521
Letzte Woche
1
Letzten Monat
14
checked on 17.11.2018

Download(s)

212
checked on 17.11.2018

Google ScholarTM

Prüfe

Export

Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.