Titel: Elastic behaviour at the nanoscale of innovative composites of nanoporous gold and polymer
Sprache: English
Autor/Autorin: Griffiths, Emma 
Bargmann, Swantje 
Reddy, B. Dayanand 
Schlagwörter: nanocomposite;homogenization;micromechanics;hierarchical materials
Erscheinungsdatum: 27-Sep-2017
Verlag: Elsevier
Quellenangabe: Extreme Mechanics Letters (17): 16-23 (2017)
Zeitschrift oder Schriftenreihe: Extreme Mechanics Letters 
Zusammenfassung (englisch): Nanoporous gold is a material with unique properties that make it attractive for use in multiple areas. It has an extremely high compressive strain capability but is very brittle in tension which limits its usage. One means of addressing this limitation is to fill the voids of the nanoporous material with a polymer, resulting in a more ductile and stronger material. In this work, the mechanical properties of a nanocomposite representative sample are studied numerically. The study is based on homogenization with the use of three types of boundary conditions. The stress–strain response within the composite is also analysed. Under a pure compression test, the sample shows both compressive and tensile strains and stresses. This is due to the complex interaction within the microstructure. Within the composite, the polymer is still considerably more compliant than the gold material showing much higher strains. The resultant forces, moments and torques acting on representative ligament cross-sections are also investigated under compressive loading. Bending moments and normal forces dominate the modes of loading. Ligaments along the compression axis show markedly higher normal forces compared to ligaments perpendicular to this axis. The normal stress distributions of the ligaments show clear trends towards combined bending and normal forces while there is no discernible pattern to the shear stress distributions. These nevertheless generate high shear forces and torques.
URI: http://tubdok.tub.tuhh.de/handle/11420/1627
DOI: 10.15480/882.1624
ISSN: 2352-4316
Institut: Werkstoffphysik und -technologie M-22 
Dokumenttyp: (wissenschaftlicher) Artikel
Enthalten in den Sammlungen:tub.dok

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
1-s2.0-S2352431617301359-main.pdfVerlags-PDF3,14 MBAdobe PDFMiniaturbild
Öffnen/Anzeigen
Zur Langanzeige

Seitenansichten

64
Letzte Woche
0
Letzten Monat
checked on 21.05.2018

Download(s)

8
checked on 21.05.2018

Google ScholarTM

Prüfe

Altmetric


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.