Titel: A principle curvatures analysis of the isothermal evolution of nanoporous gold: Quantifying the characteristic length-scales
Sprache: English
Autor/Autorin: Ziehmer, Markus 
Hu, Kaixiong 
Wang, Ke 
Lilleodden, Erica 
Schlagwörter: nanoporous gold;principle curvatures;microstructure evolution;focused ion beam tomography;self-similarity
Erscheinungsdatum: 16-Aug-2016
Verlag: Elsevier
Quellenangabe: Acta Materialia (120): 24-31 (2016)
Zeitschrift oder Schriftenreihe: Acta Materialia 
Zusammenfassung (englisch): A study of the isothermal evolution of a nanoporous gold (npg) microstructure after dealloying has been performed. In order to adequately characterize its complex three-dimensional bicontinuous ligamentring structure, an analysis of the scaled principle curvatures k1 and k2 based on representative volumes of meshed 3D reconstructions was applied. Five npg samples, as obtained from an electrolytical dealloying process, with different mean ligament diameters ranging from ca. 25 nm (as-dealloyed) to ca. 420 nm (from annealing at 300 C) were analyzed. The results indicate that ligament surface flattening effects lead to small but distinct morphological changes during the investigated early and mid-stages of coarsening, visible in the scaled k1- and k2- marginal distributions. Thus, strictly speaking, self-similar evolution of npg cannot be confirmed, but dependent on the specific application, the evolution might be seen as “sufficiently” self-similar. Moreover, it is shown that the inverse mean principle curvatures from the marginal distributions can be used to identify the mean sizes of the two salient structural features, namely the ligaments and the rings. Both inverse mean principle curvatures scale linearly with the mean ligament diameter. Thus, for the material used in this study, one parameter is sufficient to characterize its microstructure. Finally, it is shown that rings resembling the ones from the real samples can be generated computationally by applying modified torus parameterizations. Surprisingly, a calculation of the curvature distribution of only one ”average” ring is sufficient to approximate the scaled kappa distributions accumulated from the ring distributions of the real samples.
URI: http://tubdok.tub.tuhh.de/handle/11420/1694
DOI: 10.15480/882.1691
ISSN: 1359-6454
Institut: Keramische Hochleistungswerkstoffe M-9 
Werkstoffphysik und -technologie M-22 
Dokumenttyp: (wissenschaftlicher) Artikel
Enthalten in den Sammlungen:tub.dok

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
1-s2.0-S1359645416306061-main.pdfVerlags-PDF1,9 MBAdobe PDFMiniaturbild
Öffnen/Anzeigen
Zur Langanzeige

Seitenansichten

38
Letzte Woche
1
Letzten Monat
0
checked on 23.09.2018

Download(s)

8
checked on 23.09.2018

Google ScholarTM

Prüfe


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.