Titel: Nanoporous-gold-based composites : toward tensile ductility
Sprache: English
Autor/Autorin: Wang, Ke 
Kobler, Aaron 
Kübel, Christian 
Jelitto, Hans 
Schneider, Gerold A. 
Weißmüller, Jörg 
Schlagwörter: ductility;nanoporous gold
Erscheinungsdatum: 12-Jun-2015
Verlag: Macmillan Publishers Limited, part of Springer Nature
Quellenangabe: NPG Asia Materials 6 (7): e187 (2015)
Zeitschrift oder Schriftenreihe: NPG Asia materials 
Zusammenfassung (englisch): We report on mechanical tests on interpenetrating-phase nanocomposite materials made by vacuum impregnation of nanoscale metal networks with a polymer. The metal component is nanoporous gold made by dealloying, whereas two epoxy resins and polyurethane are explored as the polymer component. The composites are strong and deformable in compression. Although previous observations invariably indicate tensile brittleness for nanoporous gold, composite samples made from cm-sized nanoporous samples enable macroscopic tensile and four-point bending tests that show ductility. This implies that the high strength of individual metal objects such as nanowires can now be incorporated into a strong and ductile material from which macroscopic things can be formed. In fact, a rule-of-mixture-type analysis of the stresses carried by the metal phase suggests quantitative agreement with data reported from separate experiments on small-scale gold nanostructures.
URI: http://tubdok.tub.tuhh.de/handle/11420/1704
DOI: 10.15480/882.1701
ISSN: 1884-4057
Institut: Keramische Hochleistungswerkstoffe M-9 
Werkstoffphysik und -technologie M-22 
Dokumenttyp: (wissenschaftlicher) Artikel
Enthalten in den Sammlungen:tub.dok

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
am201558.pdfVerlags-PDF2,89 MBAdobe PDFMiniaturbild
Öffnen/Anzeigen
Zur Langanzeige

Seitenansichten

40
Letzte Woche
0
Letzten Monat
5
checked on 23.09.2018

Download(s)

5
checked on 23.09.2018

Google ScholarTM

Prüfe


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.