Verlagspublikation: Journal of the European Ceramic Society Volume 29, Issue 9, June 2009, Pages 1729-1733
Verlagslink: http://dx.doi.org/10.1016/j.jeurceramsoc.2008.10.012
Titel: Effect of MnO2 on the dielectric and piezoelectric properties of Alkaline Niobate based lead free piezoelectric ceramics
Sprache: en
Autor/Autorin: Mgbemere, Henry Ekene 
Herber, Ralf-Peter 
Schneider, Gerold A. 
Schlagwörter: KNN-Keramik, synthese, piezokeramik, bleifrei;Ceramics, Piezoelectric ceramics, lead-free
Erscheinungsdatum: 2009
Quellenangabe: Journal of the European Ceramic Society Volume 29, Issue 9, June 2009, Pages 1729-1733
Zusammenfassung (englisch): Lead free ferroelectric ceramics of the KNN–LiTaO3–LiSbO3 system were prepared using the mixed oxide route. This work reports the effect of doping (K0.44Na0.52Li0.04)(Nb0.86Ta0.1Sb0.04)O3 produced through the conventional solid state sintering method with different amounts of MnO2. With 1 mol% of the dopant, ~ 96.5% of the theoretical density of the ceramics was achieved while grain growth inhibition was attained through pinning of the grain boundary movement. A polymorphic phase transition (PPT) was induced in the ceramic from the orthorhombic crystal structure to the tetragonal structure with increasing dopant amount. At lower temperatures, the doped samples had higher epsilon values but there was a decrease in both Tc (from 333 ◦C to 249 ◦C) and epsilon value at Tc (from ≈9500 to <6000). At temperatures below 300 ◦C however, the loss tangent in the doped samples (≈2.5 mol%) was much lower and steady when compared to the undoped one. The ferroelectric properties were slightly lowered with the addition of MnO2. The remnant polarisation (Pr) was lowered from ~18μC/cm2 to ~9μC/cm2, the coercive field (Ec) from ~ 8.5 kV/cm to ~ 6.2 kV/cm and the piezoelectric charge coefficient (d33) decreased as well.
URI: http://tubdok.tub.tuhh.de/handle/11420/748
DOI: 10.15480/882.746
Institut: Keramische Hochleistungswerkstoffe M-9
Advanced Ceramics M-9
Dokumenttyp: ResearchPaper
Enthalten in den Sammlungen:tub.dok

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
Effect_of_MnO2_on_the_dielectric_and_piezoelectric_propert.pdf853,04 kBAdobe PDFMiniaturbild
Öffnen/Anzeigen
Zur Langanzeige

Seitenansichten

454
Letzte Woche
1
Letzten Monat
checked on 25.11.2017

Download(s)

202
checked on 25.11.2017

Google ScholarTM

Prüfe

Altmetric


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.